AISI 304L austenitic stainless steel with different grain sizes of 0.5 -12 μm was obtained through the martensitic process. Corrosion behavior of different samples was investigated in a 0.5M HCl solution using open circuit ...

Low stacking fault energy face centered cubic (FCC) materials contain characteristic defect structures. Stacking fault tetrahedral are one of those rare structures that occur under special experimental conditions. For the ...

The aim of conducting this research was to evaluate the viscosity change in the continuous casting of steel mold powders by altering their chemical compositions, using hot stage microscope analysis. 4 low-fluorine samples ...

Deep cryogenic heat treatment is assumed as a supplementary heat treatment performed on steels before the final tempering treatment to enhance the wear resistance and hardness of the steels. In this study, the effects of ...

In this study, the effect of cold rolling process on the microstructure and texture evolution in 1wt. % Si non-oriented electrical steel was investigated. For this purpose, all samples were processed through single-stage ...

In the present study, the effects of growth defects and chromium content loss on the degradation of corrosion and passivation of cathodic arc evaporation (CAE-PVD) of stainless steel coating were investigated in 2 M sulphuric ...

The aim of the present study was to investigate the effect of quenching and tempering temperatures on the microstructure, mechanical properties and the wear characteristics of medium carbon-high chromium wear resistant ...