The effects of thickness on magnetic properties of FeCuNbSiB sputtered thin films
نوع مدرک
TextArticle
زبان مدرک
Englishچکیده
Thin films of Fe73.1Cu1Nb3.1Si14.7B8.2 alloy having thickness of 200, 500 and 800 nm have been deposited by RF sputtering. Their magnetic properties have been characterized using alternating gradient field magnetometer (AGFM) and vibrating sample magnetometer (VSM). The effects of residual stresses investigated by nanoindentation experiments were conducted on as-deposited samples. It is observed that the coercivity of as-deposited films is inversely proportional to the thickness in relation with the residual stress induced during sputtering.
کلید واژگان
Magnetic propertiesThin films
Ion sputtering
Residual stresses
Nanoindentation
Nanotechnology
شماره نشریه
6تاریخ نشر
2017-12-011396-09-10
ناشر
Sharif University of Technologyسازمان پدید آورنده
Institute for Nanoscience and Nanotechnology, Sharif University of Technology, 113658639 Tehran, IranIstituto Nazionale di Ricerca Metrologica (INRIM), I-10135 Torino, Italy
Istituto Nazionale di Ricerca Metrologica (INRIM), I-10135 Torino, Italy
Department of Chemistry and NIS, University of Turin, I-10125 Torino, Italy
Department of Chemistry and NIS, University of Turin, I-10125 Torino, Italy
Department of Materials Science and Engineering, Sharif University of Technology, 1458889694 Tehran, Iran
شاپا
1026-30982345-3605