Synthesis and Characterization of γ-Alumina Porous Nanoparticles from Sodium Aluminate Liquor with Two Different Surfactants
دریافت مدرک
FullText
اندازه فایل:
1.170 مگابایتنوع فايل (MIME):
PDFنوع مدرک
TextResearch Paper
زبان مدرک
Englishچکیده
Among the various phases of alumina, two phases γ and α are the most widely used in variousindustries. In this paper, γ-Al2O3 porous nanoparticles have been successfully synthesized from a simpleaqueous sol–gel method using inexpensive material such as: sodium aluminate liquor, HCl, NaOH,Polyethylene glycol (PEG) and polyvinyl alcohol (PVA). Sodium aluminate liquor was extracted fromBayer liquor of alumina product processed in the Jajarm alumina factory. PEG and PVA were used asstructure-stabilizing agents. The structures and properties of samples calcined at 800 ºC, wereperformed utilizing X-ray diffraction (XRD), infrared spectroscopy (FTIR), scanning electronmicroscopy (SEM), termogeravimetery analysis (TG/DTA), and N2 adsorption/desorption techniques.Prepared sample of γ-Al2O3 with polyethylene glycol surfactant has an average crystallite size of 2.313nm, average particle size of 20 nm, specific surface area (SSA) of 138.8 m2/g, and pore volume of ∼0.166 cm3/g. The average crystallite size of 2.063 nm, average particle size of 46 nm, specific surfacearea of 201.1 m2/g, and pore volume of ∼ 0.246 cm3/g, were achieved using polyvinyl alcohol surfactant.
کلید واژگان
γ-aluminaPorous
Sodium aluminate liquor
nanoparticles
surfactant
شماره نشریه
4تاریخ نشر
2016-11-011395-08-11
ناشر
Iranian Nanotechnology Societyسازمان پدید آورنده
Department of Chemistry, Faculty of Science, Bu-Ali Sina University, P.O.Box 651783868, Hamadan, IranDepartment of Engineering, Faculty of Engineering, Imam Khomeini International University, P.O. Box 3414916818, Qazvin, Iran
Department of Engineering, Faculty of Engineering, Imam Khomeini International University, P.O. Box 3414916818, Qazvin, Iran
Department of Chemistry, Faculty of Science, Bu-Ali Sina University, P.O.Box 651783868, Hamadan, Iran
Department of Chemistry, Faculty of Science, Bu-Ali Sina University, P.O.Box 651783868, Hamadan, Iran
Department of Engineering, Faculty of Engineering, Imam Khomeini International University, P.O. Box 3414916818, Qazvin, Iran
Department of Civil Engineering, Faculty of Civil Engineering , Civil Engineering College of Hamedan P.O. Box 6515735617, Hamedan, Iran
شاپا
1735-70042423-5911