Synthesis of TiC-Al2O3 Nanocomposite from Impure TiO2 by Mechanical Activated Sintering

Abstract

In this research, the production possibility of TiC-Al2O3 nanocomposite, as a useful ceramic from commercially pure TiO2, aluminum powder and carbon black has been investigated. Routile (TiO2) with carbon black and aluminum were placed in a high energy ball mill and sampled during different milling times. Then, the activated powders were synthesized at different temperatures in an atmosphere control tube furnace. Our results show that using this method has decreased the synthesizing temperature to 1000-1250˚C by increasing the milling time. Also the width of X-ray patterns peaks, had made it apparent that, the size of produced TiC crystals was in order of nanometer. Furthermore it was detected that the lattice parameter deviated slightly from the standard size.